TYPICAL DATA OF
TRIREX UT3017L
| PROPERTY | UNIT | ISO METHOD | TRIREX UT3017L |
| PHYSICAL | |||
| Melt Flow Rate (300C, 1.20kg) | g/10min | ISO 1183 | 37 |
| Specific Gravity | - | ISO 1183 | 1.19 |
| MECHANICAL | |||
| Tensile strength | MPa | ISO 527 | 64 |
| Elongation | % | ISO 527 | 75 |
| Flexural strength | MPa | ISO 178 | 94 |
| Flexural modulus | MPa | ISO 178 | 2,350 |
| lzod Impact Strength，notched，23℃ | kJ/m² | ISO 180 | 11.5 |
| lzod Impact Strength，notched，-10℃ | kJ/m² | ISO 180 | 10.3 |
| OPTICAL | |||
| Yellow Index(6mm) | - | - | 1.17 |
| Transmmitance | % | - | 92 |
| THERMAL | |||
| HDT, 1.82MPa | ℃ | ISO 75-2 | 116 |
| ※ The figures listed in this table are typical values obtained under the standard test methods and may not be applicable for products that are under different application condition. | |||
PROCESSING GUIDE FOR
TRIREX UT3017L GRADE
| SPECIFICATION | UNIT | CONDITIONS |
| Drying Temperature | ℃ | 100 |
| Drying Time | hr | 3~5 |
| Moisture Content, Max | % | 0.02 |
| Melt Temperature | ℃ | 245~265 |
| Nozzle Temperature | ℃ | 245~265 |
| Front Temperature | ℃ | 245~265 |
| Middle Temperature | ℃ | 240~255 |
| Rear Temperature | ℃ | 235~250 |
| Mold Temperature | ℃ | 60~100 |
| Back Pressure | % | <70 |
| Screw Speed | % | <60 |
| Injection Pressure | % | <70 |
| Injection Speed | % | <50 |
| Hold Pressure | % | <50 |
| Injection Cushion | Mm | 3~6 |
|
• General processing conditions for TRIREX UT3017L are shown below. • Drying prior to processing is essential to ensure desired appearance and property performance. |
||