| PROPERTY | UNIT | ASTM METHOD | TYPICAL DATA |
| PHYSICAL | |||
| Specific Gravity | - | D792 | 1.08 |
| Water Absorption (24 hours at 23℃) | % | D570 | - |
| Melt Flow Rate (260℃, 5.0kg) | g/10min | D1238 | 12 |
| MECHANICAL | |||
| Tensile Strength at yield | kgf/cm² | D638 | 430 |
| Tensile Elongation at break | % | D638 | 130 |
| Flexural Strength at yield | kgf/cm² | D790 | 650 |
| Flexural Modulus | kgf/cm² | D790 | 18,000 |
| Izod Impact Strength, notched, 23℃(1/8") | kgf.cm/cm | D256 | 55 |
| THERMAL | |||
| HDT, 18.6 kgf/cm² | ℃ | D648 | 100 |
| OTHERS | |||
| UL-94 Flammability | - | (UL 94) | HB |
| Mold Shrinkage | % | D955 | 0.5~0.7 |
| ※ The figures listed in this table are typical values obtained under the standard test methods and may not beapplicable for products that are under different application condition. | |||
PROCESSING GUIDE FOR
TRILOY 200 PG2 GRADE
| SPECIFICATION | UNIT | CONDITIONS |
| Drying Temperature | ℃ | 90 |
| Drying Time | hr | 3~4 |
| Moisture Content, Max | % | 0.02 |
| Melt Temperature | ℃ | 245~275 |
| Nozzle Temperature | ℃ | 250~270 |
| Front Temperature | ℃ | 250~270 |
| Middle Temperature | ℃ | 240~260 |
| Rear Temperature | ℃ | 220~240 |
| Mold Temperature | ℃ | 50~100 |
| Back Pressure | MPa | 0.3~0.7 |
| Screw Speed | % | 30~60(slow to moerate) |
| Vent Depth | mm | 0.02~0.08 |
|
• General processing conditions for TRILOY 200 PG2 are shown below. • Drying prior to processing is essential to ensure desired appearance and property performance. |
||