中文简介：LEXAN 953A聚碳酸酯（PC）树脂是一种无填充、可注塑的等级。这种溴化阻燃PC具有V0 UL等级，并且是紫外线稳定的，提供了额外的耐候性。LEXAN 953A树脂有有限的透明和有色选项，是一种通用树脂，是各种应用的理想选择。作为一种非氯化、非溴化阻燃剂溶液，LEXAN 955AU树脂可以被视为一种替代品。
英文简介：LEXAN 953A Polycarbonate (PC) resin is a non-filled, injection moldable grade. This brominated flame retardant PC has a V0 UL rating and is UV stabilized, providing additional weathering capability. LEXAN 953A resin is available in limited transparent and tinted color options and is a general-purpose resin that is an excellent candidate for a wide variety of applications. As a non-chlorinated, non-brominated flame retardant solution, LEXAN 955AU resin could be considered an alternative.
热线：15366296797
传真：0512-68032628
QQ：648948216
联系邮箱：abel.liu@e-sdcx.com
地址:苏州工业园区澄湾路19号 中新科技大厦16楼
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.21 g/cc | 1.21 g/cc | ASTM D792 |
| 密度 | 1.217 g/cc | 0.04397 lb/in³ | ASTM D792 |
| 吸水率 |
0.15 %
@Time 86400 sec
|
0.15 %
@Time 24.0 hour
|
ASTM D570 |
| 平衡吸湿 | 0.35 % | 0.35 % | ASTM D570 |
|
0.58 %
@Temperature 100 °C
|
0.58 %
@Temperature 212 °F
|
ASTM D570 | |
| 线性成型收缩率,Flow |
0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0050 - 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| 熔体流动速率 |
7.0 g/10 min
@Load 1.20 kg, Temperature 300 °C
|
7.0 g/10 min
@Load 2.65 lb, Temperature 572 °F
|
ASTM D1238 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 洛氏硬度（M 级） | 70 | 70 | ASTM D785 |
| 洛氏硬度（R 级） | 118 | 118 | ASTM D785 |
| 抗张强度(断裂) | 55.0 MPa | 7980 psi | Type I, 50 mm/min; ASTM D638 |
| 抗张强度(屈服) | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 90 % | 90 % | Type I, 50 mm/min; ASTM D638 |
| 屈服伸长率 | 7.0 % | 7.0 % | Type I, 50 mm/min; ASTM D638 |
| 弯曲强度 | 91.0 MPa | 13200 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 弯曲模量 | 2.24 GPa | 325 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| 悬壁梁无缺口冲击强度 | 32.04 J/cm | 60.02 ft-lb/in | ASTM D4812 |
| 拉伸冲击强度 | 525 kJ/m² | 250 ft-lb/in² | Type S; ASTM D1822 |
| 落锤总能量 | 169 J | 125 ft-lb | ASTM D3029 |
| 泰伯磨损，毫克/1000次 | 10 | 10 | CS-17, 1 kg; ASTM D1044 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | ASTM D257 |
| 介电常数 |
2.96
@Frequency 1.00e+6 Hz
|
2.96
@Frequency 1.00e+6 Hz
|
ASTM D150 |
|
3.01
@Frequency 50.0 - 60.0 Hz
|
3.01
@Frequency 50.0 - 60.0 Hz
|
ASTM D150 | |
| 介电强度 |
16.7 kV/mm
@Thickness 3.20 mm
|
424 kV/in
@Thickness 0.126 in
|
in air; ASTM D149 |
| 耗散因数 |
0.00090
@Frequency 50.0 - 60.0 Hz
|
0.00090
@Frequency 50.0 - 60.0 Hz
|
ASTM D150 |
|
0.010
@Frequency 1.00e+6 Hz
|
0.010
@Frequency 1.00e+6 Hz
|
ASTM D150 | |
| 耐电弧性 | 0.00 - 60 sec | 0.00 - 60 sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 175 - 250 V | 175 - 250 V | UL 746A |
| 热丝引燃 (HWI) | 30 - 60 sec | 30 - 60 sec | UL 746A |
| 高电弧燃烧，HAI | 30 - 60 arcs | 30 - 60 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 |
68.4 µm/m-°C
@Temperature -40.0 - 95.0 °C
|
38.0 µin/in-°F
@Temperature -40.0 - 203 °F
|
ASTM E 831 |
| 导热系数 | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | ASTM C177 |
| 载荷下热变形温度(0.46 MPa) |
137 °C
@Thickness 6.40 mm
|
279 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) |
132 °C
@Thickness 6.40 mm
|
270 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 |
| 维卡软化温度 | 151 °C | 304 °F | Rate B/50; ASTM D1525 |
| UL RTI | 130 °C | 266 °F | UL 746B |
| UL RTI，机械冲击 | 120 °C | 248 °F | UL 746B |
| UL RTI，机械无冲击 | 130 °C | 266 °F | UL 746B |
| 可燃性(UL94) |
V-2
@Thickness 1.47 mm
|
V-2
@Thickness 0.0579 in
|
UL 94 |
|
V-0
@Thickness 2.99 mm
|
V-0
@Thickness 0.118 in
|
UL 94 |
| 光学性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 折射率 | 1.586 | 1.586 | ASTM D542 |
| 雾度 |
1.0 %
@Thickness 2.54 mm
|
1.0 %
@Thickness 0.100 in
|
ASTM D1003 |
| Transmission, Visible | 85 % | 85 % | 2.54 mm; ASTM D1003 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Specific Volume | 0.83cm^3/g | ASTM D792 |
| UV-light, water exposure/immersion | F1 | UL 746C |