| PROPERTY | UNIT | ASTM METHOD | TYPICAL DATA |
| PHYSICAL | |||
| Specific Gravity | - | D792 | 1.18 |
| Water Absorption (24 hours at 23℃) | % | D570 | - |
| Melt Flow Rate (250℃, 5.0kg) | g/10min | D1238 | 22 |
| MECHANICAL | |||
| Tensile Strength @Max Load | kgf/cm² | D638 | 540 |
| Tensile Elongation @Break | % | D638 | 100 |
| Flexural Strength @Yield | kgf/cm² | D790 | 900 |
| Flexural Modulus | kgf/cm² | D790 | 24,000 |
| Izod Impact Strength（Notched 1/8"，R/T) | kgf.cm/cm | D256 | 65 |
| Rockwell Hardness | R scale | D785 | - |
| THERMAL | |||
| HDT, 18.6 kgf/cm² | ℃ | D648 | 112 |
| OTHERS | |||
| UL-94 Flammability | - | (UL 94) | HB@1.5mm |
| Mold Shrinkage | % | D955 | 0.5~0.7 |
| ※ The figures listed in this table are typical values obtained under the standard test methods and may not beapplicable for products that are under different application condition. | |||
PROCESSING GUIDE FOR
TRILOY 215S GRADE
| SPECIFICATION | UNIT | CONDITIONS |
| Drying Temperature | ℃ | 100 |
| Drying Time | hr | 4~5 |
| Moisture Content, Max | % | - |
| Melt Temperature | ℃ | 255~270 |
| Nozzle Temperature | ℃ | 250~270 |
| Front Temperature | ℃ | 250~270 |
| Middle Temperature | ℃ | 240~260 |
| Rear Temperature | ℃ | 220~240 |
| Mold Temperature | ℃ | 50~80 |
| Injection Pressure | MPa | 90~150 |
| Injection Speed | % | 30~60 |
| Back Pressure | MPa | 0.3~0.7 |
| Screw Speed | Rpm | 80~100 |
|
• General processing conditions for TRILOY 215S are shown below. • Drying prior to processing is essential to ensure desired appearance and property performance. |
||